Mea hana → degreasing → holoi wai → pickling → holoi wai → hoʻokomo i loko o ke kōkua plating solvent → hoʻomaloʻo a me ka hoʻomaʻamaʻa mua → hoʻomaloʻo wela → hoʻopau → hoʻoluʻu → passivation → holoi ʻana → hoʻomaloʻo → nānā.
(1) Degreasing
Hiki ke hoʻohana ʻia ka mea hoʻomaʻemaʻe hoʻomaʻemaʻe metala a i ʻole nā ​​​​mea hoʻomaʻemaʻe wai e hoʻomaʻemaʻe a hiki i ka pulu ʻana o ka mea hana i ka wai.
(2) Piʻi ʻana
Hiki ke ʻohi ʻia me H2SO4 15%, thiourea 0.1%, 40~60℃ a i ʻole HCl 20%, hexamethylenetetramine 1~3g/L, 20~40℃. Hiki i ka hoʻohui ʻana o ka mea hoʻopuʻi corrosion ke pale i ka matrix mai ka over-corrosion a hoʻemi i ka absorption hydrogen o ka matrix hao. ʻO ka hoʻomaʻemaʻe maikaʻi ʻole ʻana a me ka mālama ʻana i ka pickling e hoʻopili maikaʻi ʻole i ka uhi ʻana, ʻaʻohe pani zinc a ʻili paha o ka papa zinc.
(3) ʻO ke kuʻekuʻe ʻana
ʻIke pū ʻia ʻo ia ka mea hoʻopaʻa paʻa, hiki iā ia ke hoʻomau i ka ʻāpana hana ma mua o ka hoʻopaʻa ʻia ʻana e hoʻomaikaʻi i ka hoʻopaʻa ʻana ma waena o ka papa paʻi a me ka substrate. NH4Cl 15%~25%, ZnCl2 2.5%~3.5%, 55~65℃, 5~10min. I mea e hōʻemi ai i ka NH4Cl volatilization, hiki ke hoʻohui kūpono i ka glycerin.
(4) Ka maloʻo a me ka hoʻomehana mua
No ka pale ʻana i ka mea hana mai ka deforming ma muli o ka piʻi ʻana o ka mahana i ka wā o ka hoʻopaʻa ʻia ʻana, a me ka wehe ʻana i ke koena o ka wai, e pale aku i ka pahū zinc, ka hopena o ka pahū wai zinc, ʻo ka preheating maʻamau 120-180 ° C.
(5) ʻO ka galvanizing wela
Pono e hoʻomalu i ka mahana o ka solution zinc, ka manawa o ke kuʻiʻana a me ka wikiwiki o ka laweʻiaʻana o ka mea hana mai ka hopena zinc. He haʻahaʻa loa ka mahana, ʻilihune ka wai o ka wai zinc, mānoanoa a ʻaʻohe kūlike ka uhi ʻana, maʻalahi ka hana ʻana i ka sagging, a maikaʻi ʻole ka hiʻohiʻona; kiʻekiʻe ka mahana, maikaʻi ka wai o ka wai zinc, maʻalahi ka hoʻokaʻawale ʻana i ka wai zinc mai ka mea hana, a ua hoʻemi ʻia ke ʻano o ka sagging a me nā wrinkles. ʻO ka ikaika, ka uhi lahilahi, ka helehelena maikaʻi, ka hana kiʻekiʻe; akā naʻe, inā kiʻekiʻe loa ka mahana, e pōʻino loa ka mea hana a me ka ipu hao, a e hana ʻia ka nui o ka zinc dross, kahi e hoʻopilikia ai i ka maikaʻi o ka papa zinc dipping a ʻai i ka nui o ka zinc. Ma ka mahana like, lōʻihi ka manawa o ka hoʻopaʻa ʻana a me ka mānoanoa o ka papa hoʻopulapula. Ke koi ʻia ka mānoanoa hoʻokahi i nā mahana like ʻole, lōʻihi ka manawa no ka hoʻopaʻa ʻana i ke ana wela kiʻekiʻe. I mea e pale aku ai i ka hoʻololi ʻana o ka wela kiʻekiʻe o ka mea hana a hoʻemi i ka lepo zinc i hoʻokumu ʻia e ka hao hao, hana ka mea hana maʻamau i ka 450 ~ 470 ℃, 0.5 ~ 1.5min. Ke hoʻohana nei kekahi mau hale hana i nā wela kiʻekiʻe no nā mea hana nui a me nā hoʻoheheʻe hao, akā e pale i ka pae wela o ka poho hao kiʻekiʻe. I mea e hoʻomaikaʻi ai i ka wai o ka wai wela wela i nā haʻahaʻa haʻahaʻa, e pale i ka uhi ʻana mai ka mānoanoa loa, a hoʻomaikaʻi i ke ʻano o ka uhi, hoʻohui pinepine ʻia ka 0.01% a 0.02% o ka alumini maʻemaʻe. Pono e hoʻohui ʻia ka alumini i nā manawa liʻiliʻi.
(6) hoʻopau
ʻO ka hoʻopau ʻana i ka mea hana ma hope o ka hoʻopaʻa ʻana, ʻo ka wehe ʻana i ka zinc a me nā nodules zinc, ma ka lulu a i ʻole nā ​​hana lima.
(7) Ka hoʻohalahala
ʻO ke kumu o ka hoʻomaikaʻi ʻana i ke kūʻē ʻana i ka corrosion o ka lewa ma ka ʻili o ka mea hana, hoʻemi a hoʻolōʻihi paha i ke ʻano o ka ʻōpala keʻokeʻo, a mālama i kahi hiʻohiʻona maikaʻi o ka uhi. Hoʻopili ʻia lākou a pau me ka chromate, e like me Na2Cr2O7 80~100g/L, sulfuric acid 3~4ml/L.
(8) Hooluolu
Hoʻomaʻalili ʻia i ka wai, akā ʻaʻole pono e haʻahaʻa ka wela e pale ai i ka mea hana, ʻoi aku ka hoʻolei ʻana, mai ka haki ʻana i ka matrix ma muli o ke anuanu a me ka emi ʻana.
(9) Nānā
ʻO ka hiʻohiʻona o ka uhi he mālamalama, kikoʻī, ʻaʻohe sagging a wrinkles. Hiki i ka nānā mānoanoa ke hoʻohana i ka uhi ʻana i ka mānoanoa, maʻalahi ke ʻano. Hiki ke loaʻa ka mānoanoa o ka uhi ma ka hoʻololi ʻana i ka nui o ka zinc adhesion. Hiki ke hoʻopaʻa ʻia ka ikaika hoʻopaʻa ʻana e kahi paʻi kuʻi, a pono e hoʻoheheʻe ʻia ka hāpana ma 90-180 °, a ʻaʻohe māwae a ʻili paha o ka uhi. Hiki ke ho'āʻo ʻia ma ke kuʻi ʻana me ka hāmare kaumaha.
2. ʻO ke kaʻina hana hoʻoheheʻe wela wela ʻO ke kaʻina hana hoʻoheheʻe wela wela ka hana o ka hana ʻana i ka hao-zinc ma waena o ka matrix hao a me ka papa zinc maʻemaʻe ma waho. Hoʻokumu ʻia ka ʻāpana hao-zinc alloy ma luna o ka ʻili o ka mea hana i ka wā wela-dip galvanizing. Hoʻohui maikaʻi ʻia ka hao a me ka papa zinc maʻemaʻe, a hiki ke wehewehe ʻia ke kaʻina hana: i ka wā i hoʻokomo ʻia ai ka mea hana hao i loko o ka zinc hoʻoheheʻe ʻia, ua hoʻokumu mua ʻia kahi hopena paʻa o ka zinc a me ka hao alpha (kino kino) ma ka interface. He aniani kēia i hana ʻia e ka hoʻoheheʻe ʻana i nā ʻātoma zinc i loko o ka hao kumu i loko o kahi kūlana paʻa. Hoʻohui ʻia nā ʻātoma metala ʻelua, a liʻiliʻi ka huki ʻana ma waena o nā ʻātoma. No laila, i ka hiki ʻana o ka zinc i ka saturation i loko o ka hoʻonā paʻa, hoʻokaʻawale nā ​​ʻāpana ʻelua o ka zinc a me ka hao kekahi i kekahi, a ʻo nā ʻātoma zinc i hoʻoheheʻe ʻia (a i hoʻokomo ʻia paha) i loko o ka matrix hao e neʻe i loko o ka lattice matrix, a hana mālie i kahi alloy me. hao, a hoʻopuehu ʻO ka hao a me ka zinc i loko o ka zinc hoʻoheheʻe ʻia he pūhui intermetallic FeZn13, e komo ana i lalo o ka ipu hao wela, i kapa ʻia ʻo zinc dross. Ke hoʻoneʻe ʻia ka mea hana mai ka hopena immersion zinc, hoʻokumu ʻia kahi papa zinc maʻemaʻe ma ka ʻili, ʻo ia ka aniani hexagonal. ʻAʻole ʻoi aku ka nui o ka hao ma mua o 0.003%.
ʻO ke kolu, ʻo ka hana pale ʻana o ka papa galvanized wela ʻO ka mānoanoa o ka papa electro-galvanized maʻamau 5-15μm, a ʻo ka papa wela wela ma luna o 65μm, ʻoiai ke kiʻekiʻe e like me 100μm. Loaʻa ka uhi ʻana o ka galvanizing hot-dip, ka uhi paʻa a ʻaʻohe mea hoʻohui. E like me kā mākou e ʻike ai, ʻo ka ʻenehana anti-atmospheric corrosion o ka zinc e pili ana i ka pale mechanical a me ka pale electrochemical. Ma lalo o nā kūlana corrosion o ka lewa, aia nā kiʻiʻoniʻoni pale o ZnO, Zn(OH)2 a me ka zinc carbonate kumu ma ka ʻili o ka papa zinc, hiki ke hoʻolohi i ka ʻino o ka zinc i kekahi ʻano. ʻO ke kiʻi pale (ʻike ʻia ʻo ka ʻōpala keʻokeʻo) ua pōʻino a hana ʻia kahi kiʻiʻoniʻoni hou. Ke pōʻino loa ka papa zinc a pilikia ka matrix hao, e hana ka zinc i ka pale electrochemical no ka matrix. ʻO ka mana maʻamau o ka zinc ʻo -0.76V, a ʻo ka mana maʻamau o ka hao he -0.44V. Ke hana ʻia ka zinc a me ka hao i microbattery, hoʻoheheʻe ʻia ka zinc ma ke ʻano he anode. Ua pale ʻia ma ke ʻano he cathode. ʻIke loa, ʻoi aku ka maikaʻi o ka pale ʻana i ka corrosion o ka lewa i ka hao kumu ma mua o ka electro-galvanizing.
ʻO ka hā, ʻo ka hoʻokumu ʻana i ka lehu zinc a me ka zinc slag i ka wā wela-dip galvanizing
ʻAʻole pili wale ka Zinc ash a me ka zinc dross i ka maikaʻi o ka papa immersion zinc, akā ʻo ia hoʻi ke kumu o ka uhi ʻana i ka ʻōpala a hana i nā nodules zinc. Eia kekahi, ua hoʻonui nui ʻia ke kumukūʻai o ka hot-dip galvanizing. ʻO ka maʻamau, ʻo ka hoʻohana ʻana i ka zinc he 80-120kg no 1 ton workpiece. Inā koʻikoʻi ka lehu zinc a me ka lepo, ʻoi aku ka kiʻekiʻe o ka zinc e like me 140-200kg. ʻO ka mālama ʻana i ke kalapona zinc ka mea nui e hoʻomalu i ka mahana a hoʻemi i ka scum i hana ʻia e ka oxidation o ka wai wai zinc. Hoʻohana kekahi mau mea hana hale i ke one refractory, lehu lanahu, a me nā mea ʻē aʻe. Hoʻohana nā ʻāina ʻē i nā pōpō seramika a i ʻole aniani me ka haʻahaʻa haʻahaʻa thermal conductivity, kiʻekiʻe heheʻe, haʻahaʻa kikoʻī kikoʻī, a ʻaʻohe pane me ka wai zinc, hiki ke hōʻemi i ka nalowale o ka wela a pale i ka oxidation. He maʻalahi kēia ʻano pōpō e ka mea hana, a ʻaʻole pili i ka mea hana. Ka hopena ʻaoʻao. No ka hana ʻana o ka zinc dross i loko o ka wai zinc, ʻo ia ka mea nui he zinc-iron alloy me ka maikaʻi ʻole o ka wai i hana ʻia i ka wā i hoʻoheheʻe ʻia ai ka hao i loko o ka wai zinc ma mua o ka solubility i kēia mahana. Hiki ke kiʻekiʻe i ka 95% ka nui o ka zinc i loko o ka lepo zinc, he galvanizing wela. ʻO ke kī i ke kumukūʻai kiʻekiʻe o ka zinc. Hiki ke ʻike ʻia mai ka pōʻai solubility o ka hao i loko o ka wai zinc he ʻokoʻa ka nui o ka hao i hoʻoheheʻe ʻia, ʻo ia hoʻi, ka nui o ka hao hao, ʻokoʻa i nā mahana like ʻole a me nā manawa paʻa like ʻole. Ma kahi o 500 ° C, piʻi nui ka poho hao me ka hoʻomehana a me ka manawa paʻa, kokoke i kahi pilina laina. Ma lalo a ma luna o ka laulā o 480~510 ℃, piʻi mālie ka poho hao me ka manawa. No laila, kapa ka poʻe i ka 480~510 ℃ ka wahi hoʻoheheʻe ʻino. Ma kēia pae wela, e ʻino ka wai zinc i ka mea hana a ʻo ka ipu hao ka mea koʻikoʻi loa. E hoʻonui nui ʻia ka poho o ka hao ke piʻi ka mahana ma luna o 560 ℃, a e hoʻopau ka zinc i ka matrix hao ke piʻi ka mahana ma luna o 660 ℃. . No laila, ke hana ʻia nei ka plating i nā ʻāpana ʻelua o 450-480 ° C a me 520-560 ° C.
5. Ka hoomalu ana i ka nui o ka lepo zinc
No ka ho'ēmiʻana i ka zinc dross, pono e ho'ēmi i ka hao i loko o ka zinc solution,ʻo ia ka hoʻomaka me ka ho'ēmiʻana i nā kumu o ka hao.
⑴Plating a me ka mālama ʻana i ka wela e pale i ka wahi kiʻekiʻe o ka hao hao, ʻo ia hoʻi, ʻaʻole e hana ma 480 ~ 510 ℃.
⑵ E like me ka hiki, pono e wili ʻia ka ipu hao zinc me nā pā kila me ke kalapona a me ka ʻike silika haʻahaʻa. ʻO ke kiʻekiʻe o ke kalapona e hoʻolalelale i ka ʻino o ka pā hao e ka wai zinc, a hiki i ke kiʻekiʻe kiʻekiʻe ke hoʻoikaika i ka ʻino o ka hao e ka wai zinc. I kēia manawa, hoʻohana nui ʻia nā papa kila kalapona kiʻekiʻe 08F. ʻO 0.087% (0.05%~0.11%) kona maʻiʻo kalapona, ≤0.03% ka maʻiʻo silika, a loaʻa nā mea e like me ka nickel a me ka chromium hiki ke pale i ka hao mai ka ʻino ʻia. Mai hoʻohana i ke kila kalapona maʻamau, inā ʻaʻole e nui ka hoʻohana zinc a pōkole ke ola o ka ipu hao. Ua manaʻo ʻia e hoʻohana i ka carbide silicon no ka hana ʻana i kahi pahu hoʻoheheʻe zinc, ʻoiai hiki iā ia ke hoʻonā i ka poho hao, akā he pilikia hoʻi ke kaʻina hana hoʻohālike.
⑶Ka wehe pinepine ʻana i ka slag. Hoʻokiʻekiʻe mua ʻia ka mahana i ka palena o luna o ke kaʻina hana e hoʻokaʻawale i ka zinc slag mai ka wai zinc, a laila hoʻohaʻahaʻa ʻia i lalo o ka mahana o ke kaʻina hana, i pohō ka zinc slag i lalo o ka pahu a laila lawe ʻia me. he puna. ʻO nā ʻāpana i hoʻopaʻa ʻia e hāʻule i loko o ka wai zinc pono e hoʻopakele ʻia i ka manawa.
⑷Pono e pale i ka hao i loko o ka mea hoʻopalapala i lawe ʻia i loko o ka pahu zinc me ka mea hana. E hoʻokumu ʻia ka pūhui hao ʻulaʻula ʻulaʻula i ka wā e hoʻohana ʻia ai ka mea hoʻopalapala no kekahi manawa, a pono e kānana mau ʻia. ʻOi aku ka maikaʻi o ka mālama ʻana i ka pH waiwai o ka mea hoʻolaha plating ma kahi o 5.
⑸ ʻOi aku ka liʻiliʻi ma mua o 0.01% alumini i loko o ka hoʻonā plating e hoʻolalelale i ka hana ʻana o ka lepo. ʻO ka nui kūpono o ka alumini ʻaʻole e hoʻomaikaʻi wale i ka wai o ka solution zinc a hoʻonui i ka ʻōlinolino o ka uhi, akā kōkua pū kekahi i ka hōʻemi ʻana i ka lepo zinc a me ka lepo zinc. ʻO kahi liʻiliʻi o ka alumini e lana ana ma ka ʻili wai he mea maikaʻi e hōʻemi i ka oxidation, a ʻoi aku ka nui o ka hopena i ka maikaʻi o ka uhi ʻana, e hoʻopiʻi ai i nā hemahema.
⑹ Pono ka hoʻomehana ʻana a me ka wela i mea e pale ai i ka pahū a me ka wela nui o ka wahi.